Beryllium Copper Canted Coil Spring / Spring Contact Finger

Wonder copper is capable of producing the beryllium copper springs, beryllium copper spring contact, beryllium copper contact spring, beryllium copper spring contact finger, beryllium copper spring finger contact, watch-band spring contact finger, beryllium copper clack contact finger, Multi-Contact finger, Z-forms contact finger, Spirial Contact, Strip Contact, etc… according to Customer’s drawing and available samples .
With its full suite service of custom beryllium copper canted coil spring / spring contact finger, Wonder copper can handle all your high-temperature beryllium copper spring needs with consistently top quality components. Call us today!

Beryllium Copper Canted Coil Spring / Spring Contact Finger Available products

The mainly available material of beryllium copper springs and spring contact finger are C17200 beryllium copper spring contact finger, C17500 beryllium copper spring contact finger and other spring contact components.
Beryllium Copper Canted Coil Spring / Spring Contact Finger Typical application:High Voltage Switch Gear Industry/Spring Industry/Electrical Industry

Wonder Copper Advantage

  • Class 4 Alloy has extremely high hardness and ultimate tensile strength although the electrical conductivity is lower than the Class 3 Alloy
  • Class 4 Beryllium Copper (17200, Alloy 25) is available in heat treatable tempers. Alloys are used in a wide range of applications requiring high strength and stiffness with good conductivity.
  • Typical uses include electrical/electronic connectors, current-carrying springs, precision screw machined parts, welding electrodes, bearings, plastic molds and corrosion resistant components.
  • Class 3 (C17500, Alloy 10) Alloy is generally recommended for spot welding and seam welding steels having high electrical resistance, such as stainless steels. The Class 3 Alloy is heat treatable.

Canted Coil Spring Case Studies

Excellent Properties Of Beryllium Copper Alloy
High Flexibility
High Hardness
High Strength
High Conductivity
High Thermal Conductivity
Good Molding Properties
Good Fatigue Performance
Excellent Corrosion Resistance
No Spark Impact

Chemical Composition

Executive standard:ASTM/GB/T5233-2001/EN12163(%max., unless shown as range or min.)
Numbering
Be
Co+Ni
Cu
Fe
Pb
Si
Al
C17200
1.8-2.0
Co+Ni≥0.2
Margin
0.15
-
0.15
0.15
C17300
1.8-2.0
Co+Ni≥0.2
Margin
0.15
0.2-0.6
0.15
0.15
C17500
0.4-0.7
Co 2.4-2.7
Margin
0.15
-
0.15
0.15
C17510
0.2-0.6
Co≤0.3,Ni 1.4-2.2
Margin
0.15
-
0.15
0.15
QBe2.0
1.8-2.1
Ni 0.2-0.5
Margin
0.15
0.005
0.15
0.15
BeCo1Ni1
0.4-0.7
Co 0.8-1.3,Ni 0.8-1.3
Margin
0.02
-
0.02
0.04
Mechanical properties and conductivity analysis
(AT/TF00)
Numbering
Tensile Strength /MPa
Yield Strength /MPa
Elongation %
Hardness
Conductivity %IACS
C17200
1160-1380
980-1240
3—15
36-42HRC
22-28
C17300
1160-1380
980-1240
3—15
36-42HRC
22-28
C17500
700-920
560-710
10—25
92-100HRB
45-60
C17510
700-920
560-710
10—25
92-100HRB
45-60
QBe2.0
1160-1380
980-1240
3—15
36-42HRC
18-20
BeCo1Ni1
700-920
560-710
10—25
92-100HRB
45-60
Available status
Brush Name
ASTM Name
Description
A
TB00
Solution annealing state (quenched state)
¼H
TD01
Quarter hard
½H
TD02
Half hard (semi-hard)
¾H
TD03
Three-quarters hard
H
TD04
Hard state (full hard)
AT
TF00
Standard aging heat treatment in quenched state
¼HT
TH01
Quarter hard standard aging heat treatment
½HT
TH02
Half-hard standard aging heat treatment
¾HT
TH03
Three-quarters hard standard aging heat treatment
HT
TH04
Hard standard aging heat treatment (a process of comprehensive strengthening of deformation and aging)
Note: In the Brush name:
  • "A" represents the state of solution annealing (annealed, the alloy is in the softest state, easy to be stamped and formed, and needs to be cold worked or strengthened during the direct failure period);
  • "H" stands for cold processing state (hard);
  • "T" means that the material has been aging hardened by standard heat treatment (heat treatment means the state of aging strengthening heat treatment).