Beryllium Copper Plunger Tips
Previous
Next
Wonder copper are capable of producing beryllium copper plunger tips according to Customer’s drawing and available samples or detailed inquiry.
The plunger tips are made of special copper alloys and used to shoot the fluid aluminium or magnesium into the moulds of horizontal die casting machines, the most commonly copper material can be CoCoBe, CuCoNiBe and CuNiCrSi, etc…With its full suite of Beryllium Copper Plunger Tips Machining Services, Wonder copper can handle all your plunger tips machined parts through reliability and cost savings. Request a quote today!
Plunger Tips Available products
- C17200 (Alloy 25) beryllium copper plunger tips
- C17500 (Alloy 10) beryllium copper plunger tips
- C17510 (Alloy 3) beryllium copper plunger tips
- CuCo1Ni1Be beryllium copper plunger tips
Plunger Tips Typical application
- Aluminum die casting industry
- Plastic Molding industry
Beryllium Copper Plunger tips advantage
- High Strength and higher hardeness
- lower consumption of lubricant
- improved cooling ability
- reduction of casting costs
- longer life of casting chamber/casting capacity
Plunger Tips Case Studies
-
- Plunger Tips (1)
-
- Plunger Tips (3)
-
- Plunger Tips (2)
-
- Plunger Tips (4)
Excellent Properties Of Beryllium Copper Alloy
High Flexibility
High Hardness
High Strength
High Conductivity
High Thermal Conductivity
Good Molding Properties
Good Fatigue Performance
Excellent Corrosion Resistance
No Spark Impact
Chemical Composition
Executive standard：ASTM/GB/T5233-2001/EN12163(%max., unless shown as range or min.)
Numbering
Be
Co+Ni
Cu
Fe
Pb
Si
Al
C17200
1.8-2.0
Co+Ni≥0.2
Margin
0.15
-
0.15
0.15
C17300
1.8-2.0
Co+Ni≥0.2
Margin
0.15
0.2-0.6
0.15
0.15
C17500
0.4-0.7
Co 2.4-2.7
Margin
0.15
-
0.15
0.15
C17510
0.2-0.6
Co≤0.3,Ni 1.4-2.2
Margin
0.15
-
0.15
0.15
QBe2.0
1.8-2.1
Ni 0.2-0.5
Margin
0.15
0.005
0.15
0.15
BeCo1Ni1
0.4-0.7
Co 0.8-1.3,Ni 0.8-1.3
Margin
0.02
-
0.02
0.04
Mechanical properties and conductivity analysis
(AT/TF00)
Numbering
Tensile Strength /MPa
Yield Strength /MPa
Elongation %
Hardness
Conductivity %IACS
C17200
1160-1380
980-1240
3—15
36-42HRC
22-28
C17300
1160-1380
980-1240
3—15
36-42HRC
22-28
C17500
700-920
560-710
10—25
92-100HRB
45-60
C17510
700-920
560-710
10—25
92-100HRB
45-60
QBe2.0
1160-1380
980-1240
3—15
36-42HRC
18-20
BeCo1Ni1
700-920
560-710
10—25
92-100HRB
45-60
Available status
Brush Name
ASTM Name
Description
A
TB00
Solution annealing state (quenched state)
¼H
TD01
Quarter hard
½H
TD02
Half hard (semi-hard)
¾H
TD03
Three-quarters hard
H
TD04
Hard state (full hard)
AT
TF00
Standard aging heat treatment in quenched state
¼HT
TH01
Quarter hard standard aging heat treatment
½HT
TH02
Half-hard standard aging heat treatment
¾HT
TH03
Three-quarters hard standard aging heat treatment
HT
TH04
Hard standard aging heat treatment (a process of comprehensive strengthening of deformation and aging)
Note: In the Brush name:
- "A" represents the state of solution annealing (annealed, the alloy is in the softest state, easy to be stamped and formed, and needs to be cold worked or strengthened during the direct failure period);
- "H" stands for cold processing state (hard);
- "T" means that the material has been aging hardened by standard heat treatment (heat treatment means the state of aging strengthening heat treatment).